传统的轻烧镁球的制备是将80%轻烧镁粉加入粘结剂后，放入混碾机进行碾压、搅拌、混合15～20min形成混合料，通过皮带输送机送人压球机制备出产品，然后进行堆放。轻烧镁球成品经过48h阴干并形成强度后，以备销售。

    这种镁球常见于东北和沿海地区的钢企，因为东北有丰富的菱镁矿资源，沿海地区拥有丰富的水镁石等，尤其是在某些化工企业企业，采用电解法制备氯气后的剩余物，基本上是一种工业垃圾，将其制备成为镁球价廉物美，镁球的排位较高，可以达到65%以上。 

    除此之外的其它企业，使用的镁球中间的氧化镁含量基本上在45%～65%之间。

     The traditional preparation of lightly burned magnesium balls is to add 80% lightly burned magnesium powder to the binder, put it into a mixer to roll, stir, and mix for 15-20 minutes to form a mixture, and send it to the ball through a belt conveyor Prepare the product and stack it. The finished product of light-burned magnesium spheres is dried in the shade for 48 hours and formed into strength, ready for sale.

     This kind of magnesium ball is commonly found in steel companies in the northeast and coastal areas. Because the northeast is rich in magnesite resources and the coastal areas are rich in brucite, especially in some chemical enterprises, the chlorine gas is produced by electrolytic method. The remainder is basically an industrial waste, and it is prepared into magnesium balls with low price and good quality. The ranking of the magnesium balls is higher, which can reach more than 65%.

     In other companies, the magnesium oxide content in the magnesium balls used is basically between 45% and 65%.