使用轻烧镁球的好处有哪些 What are the benefits of using lightly burned magnesium balls
发布日期:2015-12-15 00:00 来源:http://www.jialanrihua.com 点击:
使用轻烧镁球的好处有那些?轻烧镁球是一种碱性耐火制品,CaO的作用:可以取代石灰中的CaO,保证炼钢终渣碱度,减少石灰加入量。CaO能与炉渣中的SiO2反应CaO+SiO2=3CaO.SiO2、Ca2SiO4,C3S、C2S都是高熔点物质,如果炉渣中的CaO含量足够的话,轻烧氧化镁球的主要成分以MgO为主既可。 虽然通过调整炉渣中MgO的操作,可以达到降低炉渣过热度和稠化炉渣的目的,但是利用C—O反应C(FeO)=Fe+CO,降低炉渣中FeO含量和MgO的饱和溶解度,使炉渣中的MgO更容易达到或超过饱和值。从而改质炉渣既有较高的耐火度又有适宜的粘度,满足溅渣护炉的条件,因此也可以在轻烧氧化镁球中适当增碳。
What are the benefits of using lightly burned magnesium balls? Light-burned magnesium ball is an alkaline refractory product. The role of CaO: it can replace CaO in lime, ensure the alkalinity of the final steelmaking slag, and reduce the amount of lime added. CaO can react with SiO2 in the slag. CaO SiO2 = 3CaO.SiO2, Ca2SiO4, C3S, and C2S are all high-melting substances. If the content of CaO in the slag is sufficient, the main component of lightly burned magnesia balls is mainly MgO. Although the operation of MgO in the slag can be adjusted to reduce the slag superheat and thicken the slag, the C—O reaction C (FeO) = Fe CO is used to reduce the FeO content in the slag and the saturation solubility of MgO, so that the MgO is more likely to reach or exceed saturation. Therefore, the modified slag has both a higher fire resistance and a suitable viscosity, which satisfies the conditions of slag splashing to protect the furnace, so it can also appropriately increase carbon in light-burned magnesia balls.
使用轻烧镁球主要有四大好处:
1、适合溅渣护炉的炉渣碱度:R(CaO/SiO2)约3.5左右
2、合适的留渣量(吨钢):90---100Kg/t
3、适当的溅渣时间:2--4min
4、控制终渣MgO值:
5、终渣MgO含量(推荐值%)选择合适的轻烧镁球:≤MgO≧45%,根据转炉终渣情况适当调整轻烧氧化镁球的成分。
基于上述理论、实践与研究,本公司营口J9九游会官网菱镁针对炼钢的时候起到贱渣护炉的作用。增加炉龄寿命,降低炼钢成本。
There are four major benefits to using lightly burned magnesium balls:
1. Slag alkalinity suitable for slag splashing furnace: R (CaO / SiO2) is about 3.5
2. Appropriate slag retention (ton steel): 90 --- 100Kg / t
3. Appropriate slag splashing time: 2--4min
4. Control the final slag MgO value:
5. The final slag MgO content (recommended value%) Select a suitable light-burned magnesium ball: ≤MgO ≧ 45%, and adjust the composition of the light-burned magnesium oxide ball according to the condition of the converter's final slag.
Based on the above theory, practice, and research, the company's Yingkou Bohai Magnesite plays a role in protecting slag when making steel. Increase furnace life and reduce steelmaking costs.
相关标签:轻烧镁球
相关新闻:
- 轻烧镁球是应用于哪里
- 轻烧镁球行业的明天 The future of light burned magnesium ball industry
- 轻烧镁球含有什么成分 What is the content of lightly burned magnesium balls
- 炼钢废弃料制轻烧镁球工艺 Process for making light-burned magnesium balls from steelmaking waste
- 轻烧镁球如何在溅渣中护炉 How lightly burned magnesium balls protect the furnace in slag splashing
- 转变经济发展 加强企业创新 轻烧镁球资源高效合理利用 Transforming economic development, strengthening corporate innovation, efficient and rational use of light-burned magnesium balls
- 轻烧镁球烧结降镁,效益更美 Light-burned magnesium balls sinter magnesium reduction, more beautiful
- 购买轻烧镁球后,要采取保护措施 Protective measures should be taken after purchasing lightly burned magnesium balls
- 转变经济发展 加强企业创新 轻烧镁球资源高效合理利用
- 轻烧镁球如何在溅渣中护炉 How lightly burned magnesium balls protect the furnace in slag splashing